| Grade | FRX-B101 |
| Appearance | White Powder |
| Phosphorus Content (w/%) |
16-22 |
| Nitrogen Content (w/%) | 18-24 |
| Moisture (w/%) | ≤ 0.5 |
| Particle Size D50 (μm) | ≤ 25 |
| Decomposition Temperature (℃) | ≥ 280 |
Halogen free, environmental protection, low smoke and low toxicity.
Excellent flame resistance with low migration under high temperature and high humidity.
Less influence on mechanical properties.
It suitable for PP, PE, can also be uesd in TPE or other polyolefin flame retardant products.
| Materials | 1# | 2# |
|
Co PP |
50 |
50 |
| Homo PP | 24 | 24 |
| FRX-B101 | 24 | 0 |
| Comparable Product | 0 |
24 |
| Color Masterbatch | 1.5 | 1.5 |
|
Lubricant / Antioxidant |
0.5 | 0.5 |
| Anti-dripping Agent | 0.2 |
0.2 |
| Test Item | Test Standard | Unit | 1# | 2# |
| Tensile Strength | GB/T 1040-06 | Mpa |
24 |
24 |
| Elongation | GB/T 1040-06 | % | 58 | 57 |
| Flexural Modulus | GB/T 9341-08 | Mpa | 1500 | 1520 |
| Notch Impact Strength | GB/T 1043-1-08 | kJ/m2 |
8.0 |
7.9 |
| UL94 V0 Test Sample Thickness | FRX-B101 | Comparable Product | ||
|
t1 |
t2 | t1 | t2 | |
| 1.6 mm | 2.4 | 3.1 | 2.8 | 3.6 |
| 2.3 | 2.8 | 2.5 | 3.2 | |
| 2.8 | 2.6 | 3.2 | 4.2 | |
| 2.9 | 2.9 | 2.5 | 3.0 | |
| 2.1 | 2.3 | 2.6 | 3.8 | |
| t1+t2: 25.6 | t1+t2: 31.4 | |||
| 3.2 mm | 2.6 | 2.5 | 2.5 | 2.5 |
| 2.6 | 2.5 | 2.5 | 2.4 | |
| 2.7 | 2.4 | 2.8 | 2.9 | |
| 2.9 | 3.2 | 2.5 | 2.8 | |
| 2.9 | 3.2 | 2.5 | 2.8 | |
| 2.7 | 2.8 | 2.6 | 3.1 | |
| t1+t2: 26.0 | t1+t2: 26.6 | |||
It has good moisture and heat resistance without migration at 85℃ and 85% humidity for 336h in non-reinforced PP systems.
Comply with the requirements of RoHS and REACH restriction.
1. Compound paper plastic bag lined with PE film: 25kg/bag.
2. It needs to be sealed and moisture-proof, and recommended to be stored in a dry place.
3. Storage and transportation temperature: <90℃.
4. The minimum shelf life: 24 months.